XPS와 표면전위감쇠를 통한 PET 필름의 표면분석

초록

In this study, the surface properties of PET film were analyzed after plasma surface treatment. After plasma treatment of surface roughness and XPS were evaluated to analyze the chemical property, while the surface potential decay and surface resistivity was measured to analyze the electrical characteristic. When plasma discharge treatment was conductedfor less than 10 minutes, the electrical insulating property was found to be improved through evaporation of low molecular weight materials and cleaning of surface. However, when the treatment was conducted for more than 10 minutes, the insulating property was decreased due to excessive discharge energy. Analysis of chemical characteristics showed that 10-minute treatment resulted in increase of C-O and O=C-O. However, when treated for more than 10 minutes, they were relatively decreased.