Improvement of the mechanical property and specific gravity of the silicone foam filled with tannic acid

초록

Silicone foam containing tannic acid (TA) was prepared and characterized in terms of the morphological and mechanical properties, and specific gravity. SEM, EDS, and TGA analyses were applied to analyze the TA-filled silicone foam systematically. The addition of 10 wt.% of TA contributed to an increase in the expansion ratio and the reduction of the specific gravity of the silicone foam. In addition, the improvement of the Young’ s modulus and tensile strength was accomplished by the addition of chemically modified TA. The reason of the improvement of the mechanical property is the crosslinking reaction between the hydroxy group in the TA and the hydride group in the hydride-terminated polydimethylsiloxane (H-PDMS). The amount of the hydroxy-terminated PDMS could be decreased due to the addition of the chemically modified TA that provide hydroxy group be half of hydroxy-terminated PDMS. Therefore, vinyl-terminated PDMS could be readily crosslinked with H-terminated PDMS. As a result, the mechanical properties could be improved with the reduction of specific density. This work was supported by the Technology Innovation Program (20010265) funded by the Ministry of Trade, Industry and Energy (MOTIE, Korea).