Evolution of Microstructure and Mechanical Properties of Al-Zn-Mg-Cu Alloy by Extrusion and Heat Treatment

초록

Herein, composite extrusion deformation and heat treatment process at various temperatures were studied on a new type of Al-Zn-Mg-Cu alloy billet. The influence of pre-deformation and the final forming of extrusion and heat treatment of annular channel corner extrusion on the microstructure evolution and mechanical properties were explored. The results show that the extrusion process could further refine the structure and break the coarse theta phase. The grains can be refined again after the deformed sample was treated by solution-aging treatment. At the same time, a fine, dispersed second phase is precipitated around the fine recrystallized grains. This is the main reason for the increase in alloy elongation and tensile strength. The best heat treatment process parameters for the formed cup-shaped structure are 480 degrees C x 1 h solid solution and 120 degrees C x 24 h aging. The strengthening of the alloy mainly includes three mechanisms: fine grain strengthening, precipitation strengthening, and dispersion strengthening.

키워드