Comparative study of Mo and W Bonding Layers on Graphite during Plasma Spraying

초록

Graphite is useful in high-temperature applications in many engineering fields, such as heat-treating, brazing, and sintering industries. As the operation becomes severe, carbon experiences degradation leading to failure. In this study, a protective coating of W and Mo as the intermediate layer by air plasma spraying on graphite substrate was investigated to find a better intermediate layer. Their performance was explored as a bonding layer in a protective alumina-YSZ ceramic topcoat. X-ray diffraction and scanning electron microscope were used to observe the cross-section of coatings and the difference in the bonding characteristics between W and Mo, respectively. W was found inferior to Mo as a bonding performance over 1450 ℃ in view of carbide formation against the thermodynamic data. It seems to be related to the formation of a barrier layer as oxide during air plasma spraying. © © 2023 ASM International® All rights reserved.